Temperature in [°C]: 20.0 0.0
Br min 0.870 T 8.7 kG
Br nom 0.900 T 9.0 kG
HcB min 9 kA/m 0.1 kOe
HcB nom 19 kA/m 0.2 kOe
HcJ min 10 kA/m 0.1 kOe
HcJ nom 20 kA/m 0.3 kOe
BH max, min 3.2 kJ/m3 0.4 MGOe
BH max, nom kJ/m3 MGOe
α Br nom -0.010 ~ -0.035 %/°C
β HcJ nom -0.03 ~ 0.03 %/°C
T max 500 °C
ρ 6.8 g/cm3
µr 7.5
300 - 400 HV
E 100 - 200 kN/mm2
300 - 400 N/mm2
- N/mm2
11.0 - 12.0 10-6/K | - 10-6/K// - 10-6/Kρel 0.45 - 0.55 10-6 Ω.m
c - J/(kg.K)
λ 10.0 - 50.0 W/m.K
Note:
BMAsi-3/1 AlNiCo sintered
Bomatec |Hofstrasse 1 |Tel. +41 44 872 10 00 |Fax. +41 44 872 10 01 |[email protected] | www.bomatec.ch
magnetic properties
Remanence 20°C
Coercitivity 20°C
Intrinsic Coercitivity 20°C
Maximum Energy Product 20°C
Reversible Temperature Coefficient 1)
material properties (typical values)
Flexural Strength
Expansion Coefficient
Expansion Coefficient in direction of anisotropy
Specific Electric Resistance
Max. Operating Temperature 2)
Density
Permeability 20°C
1) The shown temperature coefficients are nominal reference values only . They can vary for different temperatures and don't need to be linear.
2) The maximum operating temperature is depending on the magnet shape, size and on the specific application.
The above plotted graphs are idealized and represent theoretical values of the material. Shown are curves according nominal values based
on uncoated material samples according to IEC 60404-5. Material and magnetic data represent typical data that may vary due to product
shape, size and coating. Please contact Bomatec regarding specific requirements for your application.
Vickers Hardness
Modulus of Elasticity
Copressive Strength
Specific Heat Capacity
Thermal Conductivity
4 3 2 1.5 1 0.75 0.5 0.25 0.00
0.10
0.20
0.30
0.40
0.50
0.60
0.70
0.80
0.90
1.00
-40.0 -20.0 0.0
po
lari
zati
on
J, f
lux
den
sity
B [
T]
demagnetization field H [kA/m]
-B/(µ0*H)
Version 19.10.2015