LTH - 7002 Issue date: 14.04.2014 Spec Code: LTH - 7002 Description Construction Face material Thickness Tensile strength Elongation Adhesive Adhesion Cohesion Release Liner Resistance Storage Disclaimer: Manufacturer: TEHNICAL INFORMATION White Matt Polyimide Heat Resistant Film 25 micron Polyimide based face film Acrylic adhesive. High resolution ther- mal transfer printable. Superior specification for high temperature resistance. We confirm that the material is in compliance with the requirements of the European Union Directive 2011/65/EU on the restriction of the use of certain hazardous substances in electrical and electronic equipment, also known as “RoHS". FACE STOCK Matt White Coated Polyimide Film ADHESIVE Acrylic type RELEASE LINER Poly-coated glassine with Si coating 32 μm JIS Z 1702 MD 86.3 N/15 mm JIS C 2318 CD 90.0 N/15 mm JIS C 2318 MD 158% JIS C 2318 CD 136% JIS C 2318 9.11 SI(N/25mm) JIS Z 0237 930 CGS(g/25mm) JIS Z 0237 NC 70000 (sec) see the note below. Note: Adhesion: 24 hours after application Cohesion: J. Dow Method (0 angle Dead Load Test at 40C) Applied area: 25 mm x 25 mm, 1kg load NC: Non creap Substrate: Stainless steel Color Blue Thickness 88 μm Weight 98 g/m Reading Aperture Size: 0.6 (0.006 inch) Frequency: 660 nm Evaluation: A: Excellent <--> F: Fail Avoid high humidity and high temp. Ideal condition: 10 though 30℃, less than 70% RH. Contact with water and chemical must be avoided. Direct exposure to the sunlight must be avoided. The representations of performance and suitability for use contained in this data sheet are meant only as a guide. This specifications are guaranteed by the material producer. Since only the user is aware of the speciﬁed conditions in which the product is to be used, it is the user’s responsibility to determine whether the product is suitable for that intended use. Lintec ® , Japan. Heat Time 5 mins 10 mins 30 mins 1 hr Temp. ºC 300 O X X X 250 O O O X 200 O O O O Solvents & Chemicals Ethanol IPA Toluene Ethyl Acetate Gasoline 10% Sulfuric Acid 10% Sodium Hydroxide Ricoh B110CX A A C D A A A Sony TR4070 A A F C A A A Fujicopian FSR II A A F F A A A

Upload
vodat
Category

Documents
view
213
download
0

Embed Size (px):

Transcript of LTH - 7002 - id.lthd.com · 32 μm jis z 1702 md 86.3 n/15 mm jis c 2318 cd 90.0 n/15 mm jis c 2318...

LTH - 7002

Issue date: 14.04.2014 Spec Code: LTH - 7002

Description

Construction

Face material

Thickness

Tensile strength

Elongation

Adhesive

Adhesion

Cohesion

Release Liner

Resistance

Storage

Disclaimer:

Manufacturer:

TEHNICAL INFORMATION White Matt Polyimide Heat Resistant Film

25 micron Polyimide based face film Acrylic adhesive. High resolution ther-mal transfer printable. Superior specification for high temperature resistance. We confirm that the material is in compliance with the requirements of the European Union Directive 2011/65/EU on the restriction of the use of certain hazardous substances in electrical and electronic equipment, also known as “RoHS".

FACE STOCK Matt White Coated Polyimide Film ADHESIVE Acrylic type RELEASE LINER Poly-coated glassine with Si coating 32 μm JIS Z 1702 MD 86.3 N/15 mm JIS C 2318 CD 90.0 N/15 mm JIS C 2318 MD 158% JIS C 2318 CD 136% JIS C 2318 9.11 SI(N/25mm) JIS Z 0237 930 CGS(g/25mm) JIS Z 0237 NC 70000 (sec) see the note below. Note: Adhesion: 24 hours after application Cohesion: J. Dow Method (0 angle Dead Load Test at 40C) Applied area: 25 mm x 25 mm, 1kg load NC: Non creap Substrate: Stainless steel Color Blue Thickness 88 μm Weight 98 g/m

Reading Aperture Size: 0.6 (0.006 inch) Frequency: 660 nm Evaluation: A: Excellent <--> F: Fail

Avoid high humidity and high temp. Ideal condition: 10 though 30℃, less

than 70% RH. Contact with water and chemical must be avoided. Direct exposure to the sunlight must be avoided. The representations of performance and suitability for use contained in this data sheet are meant only as a guide. This specifications are guaranteed by the material producer. Since only the user is aware of the specified conditions in which the product is to be used, it is the user’s responsibility to determine whether the product is suitable for that intended use. Lintec

®, Japan.

Heat

Time

5 mins 10 mins 30 mins 1 hr

. ºC

300 O X X X

250 O O O X

200 O O O O

Solvents & Chemicals Ethanol IPA Toluene Ethyl

Acetate Gasoline

10% Sulfuric

Acid