Technical data - DIAMANT Metallplastic GmbH
2
Technical data dichtol WF 49 #1849 Applicaon dip x brush x inject x spray x Surface temperature for applicaon [max.] 40°C Exposure me [min.] up to 5 mm wall thickness 10 5 - 10 mm 15 10 - 15 mm 20 > 15 mm 40 Curing at + 20°C [hours] load-bearing capacity light (full) Surface drying [min.] 45 up to 5 mm wall thickness 8 (16) 5 - 10 mm 10 (20) 10 - 15 mm 12 (24) > 15 mm 16 (32) Technical data Pore Size [mm] 0 - 0.5 (depending on the seng) Connuous temperature resistance [°C] -40 / +200 Short-term. Temperature resistance [°C] -40 / +220 Viscosity DIN4 cup, + 23°C ISO 2431 (4 mm nozzle) [sec.] varies according to mixture Remaining Surface layer thickness [μm] 3 - 20 (depending on the seng) All material values are average values and vary due to the mixing rao, the amount of material and the environmental condions. The values stated are based on tesng under normal condions (STP) + 20 ° C and 1013 mbar. Pore Ø (mm) Mixing rao (by weight) Viscosity DIN 2mm / 20°C Density g / ml Solid body weight 0 - 0.1 1:4 42 Seconds 0.900 approx 13.0% 0.1 - 0.5 1:3 48 Seconds 0.915 approx 17.5% > 0.5 1:2 60 Seconds 0.930 approx 25.5%
Transcript of Technical data - DIAMANT Metallplastic GmbH
Technical data dichtol WF 49 #1849
Application
dip x
brush x
inject x
spray x
Surface temperature for application [max.] 40°C
Exposure time [min.]
up to 5 mm wall thickness 10
5 - 10 mm 15
10 - 15 mm 20
> 15 mm 40
Curing at + 20°C [hours]load-bearing capacity light (full)
Surface drying [min.] 45
up to 5 mm wall thickness 8 (16)
5 - 10 mm 10 (20)
10 - 15 mm 12 (24)
> 15 mm 16 (32)
Technical data
Pore Size [mm] 0 - 0.5 (depending on the setting)
Continuous temperature resistance [°C] -40 / +200
Short-term. Temperature resistance [°C] -40 / +220
Viscosity DIN4 cup, + 23°CISO 2431 (4 mm nozzle) [sec.] varies according to mixture
RemainingSurface layer thickness [μm] 3 - 20 (depending on the setting)
All material values are average values and vary due to the mixing ratio, the amount of material and the environmental conditions. The values stated are based on testing under normal conditions (STP) + 20 ° C and 1013 mbar.
Pore Ø(mm)
Mixing ratio(by weight)
Viscosity DIN 2mm / 20°C
Densityg / ml
Solid body weight
0 - 0.1 1:4 42 Seconds 0.900 approx 13.0%
0.1 - 0.5 1:3 48 Seconds 0.915 approx 17.5%
> 0.5 1:2 60 Seconds 0.930 approx 25.5%
Resistance listChemicals Conc. in % WF 49acetate x
acetylene x
alkanes x
alcohols x
animal based oils x
brake oil x
citric acid x
crude oil x
cutting oil x
diesel fuels x
diethyl ether ─
engine oil x
glycol x
hydraulic fluid x
hydrocarbons x
aromatics x
hydrochloric acid < 20 ○
hydrochloric acid > 20 x
keton ○
kerosene x
lubricating oil x
machine oil x
machinefat x
natural gas x
nitric acid ○
petrol x
phthalates x
plantbase oils x
potassium chloride, hs x
potassium hydroxide x
potassium phosphate x
salicylic acid x
sulphuric acid < 20 ○
sulphuric acid > 20 x
Nomenclature: hs = aqueous solution / conc. = ConcentrationSymbols: x = stable / ○ = conditionally stable / ─ = unstableThe measurements were carried out at a temperature of 20°C.Individual examinations can be carried out after consultation.