KRAIBON...Compound Hard-ness (ShA) Density (g/cm³) Elongation at break (%) Tear strength (MPa)...
Transcript of KRAIBON...Compound Hard-ness (ShA) Density (g/cm³) Elongation at break (%) Tear strength (MPa)...
PRODUCT INFO
Standard CompoundsKRAIBON®
Gummiwerk KRAIBURG GmbH & Co. KG
KRAIBON®
Compound Hard-ness
(ShA)
Density(g/cm³)
Elongationat break
(%)
Tear strength
(MPa)
Rebound resilience
(%)
Dampingtan-δ-peak
(100Hz)
Curing 120 °C(min)
Curing 140 °C(min)
Curing 170 °C(min)
max.application
temperature (long term) (°C)
Resistance Application Availability Standard thickness(customized solutions
possible)
AA6CFZ 64 1,04 310 8,1 54 0,4@ - 20 °C 60 7,3 --- 120Weather resistance, limited oil and fuel resistance
Standard material Impact, friction, splinter, hinges from 10 m² 0,5
AA9CFZ 84 1,09 157 7,9 49 0,5@ - 20 °C 60 7,3 --- 120Weather resistance, limited oil and fuel resistance
Like AA6CFZ but harder, especially for impact protection and stiffness from 10 m² 0,5
AA6KFZ 65 1,03 292 12,2 65 0,6@ - 20 °C 70 7,3 --- 120
Weather resistance, limited oil and fuel resistance
Standard material in 0,35 mm Impact, friction, splinter, hinges such as AA6CFZ from 10 m² 0,35
AA9KFZ 89 1,09 129 11,1 54 0,5@ - 20 °C 64 7,3 --- 120
Weather resistance, limited oil and fuel resistance
Standard material in 0,35 mm Impact, friction, splinter, hinges like AA9CFZ from 10 m² 0,35
UT7CFZ (SUT9609/24)
73 1,13 357 7,5 20 1,1@ + 10 °C 70 8,4 --- 120
Weather resistance, limited oil and fuel resistance
Especially for acoustic applications, good drapeability, good stiffness due to hardness from 10 m² 0,5
HHZ9578/99 91 1,74 117 7,3 7 0,8@ + 25 °C 75 8 2 150
Fire, weather and oil resistance,fulfills EN45545 R1HL3
Especially for air- and railway sector due to fire resistance from 10 m² 0,4
VA6BOZ (SVA5017/41)
62 1,97 336 11,9 4 0,8@ + 20 °C 90 18 1,3 280Weather resistance, oil and fuel resitance, heat resistance
Fuel tank, application for oil/fuel contact, heat resitance from 10 m² 0,5
HAA9275/45 98 1,25 71 14,9 55 0,5@ - 20 °C 28 3 0,5 120
Weather resistance, limited oil and fuel resistance, resistance to aqueous liquids
Direct adhesion to steel, aluminium etc. from 10 m² 0,4
HVV9632/59 95 1,35 88 15,4 33 0,7@ - 0 °C 35 4,5 0,6 160 Weather resistance, oil and fuel re-sitance, average resistance to heat
Direct adhesion to steel, aluminium, polyamide etc. from 10 m² 0,5
Please note that the indicated values are subject to minor variations due to the applied raw materials and production processes.
PROPERTIES
Compound Hard-ness
(ShA)
Density(g/cm³)
Elongationat break
(%)
Tear strength
(MPa)
Rebound resilience
(%)
Dampingtan-δ-peak
(100Hz)
Curing 120 °C(min)
Curing 140 °C(min)
Curing 170 °C(min)
max.application
temperature (long term) (°C)
Resistance Application Availability Standard thickness(customized solutions
possible)
AA6CFZ 64 1,04 310 8,1 54 0,4@ - 20 °C 60 7,3 --- 120Weather resistance, limited oil and fuel resistance
Standard material Impact, friction, splinter, hinges from 10 m² 0,5
AA9CFZ 84 1,09 157 7,9 49 0,5@ - 20 °C 60 7,3 --- 120Weather resistance, limited oil and fuel resistance
Like AA6CFZ but harder, especially for impact protection and stiffness from 10 m² 0,5
AA6KFZ 65 1,03 292 12,2 65 0,6@ - 20 °C 70 7,3 --- 120
Weather resistance, limited oil and fuel resistance
Standard material in 0,35 mm Impact, friction, splinter, hinges such as AA6CFZ from 10 m² 0,35
AA9KFZ 89 1,09 129 11,1 54 0,5@ - 20 °C 64 7,3 --- 120
Weather resistance, limited oil and fuel resistance
Standard material in 0,35 mm Impact, friction, splinter, hinges like AA9CFZ from 10 m² 0,35
UT7CFZ (SUT9609/24)
73 1,13 357 7,5 20 1,1@ + 10 °C 70 8,4 --- 120
Weather resistance, limited oil and fuel resistance
Especially for acoustic applications, good drapeability, good stiffness due to hardness from 10 m² 0,5
HHZ9578/99 91 1,74 117 7,3 7 0,8@ + 25 °C 75 8 2 150
Fire, weather and oil resistance,fulfills EN45545 R1HL3
Especially for air- and railway sector due to fire resistance from 10 m² 0,4
VA6BOZ (SVA5017/41)
62 1,97 336 11,9 4 0,8@ + 20 °C 90 18 1,3 280Weather resistance, oil and fuel resitance, heat resistance
Fuel tank, application for oil/fuel contact, heat resitance from 10 m² 0,5
HAA9275/45 98 1,25 71 14,9 55 0,5@ - 20 °C 28 3 0,5 120
Weather resistance, limited oil and fuel resistance, resistance to aqueous liquids
Direct adhesion to steel, aluminium etc. from 10 m² 0,4
HVV9632/59 95 1,35 88 15,4 33 0,7@ - 0 °C 35 4,5 0,6 160 Weather resistance, oil and fuel re-sitance, average resistance to heat
Direct adhesion to steel, aluminium, polyamide etc. from 10 m² 0,5
Please note that the indicated values are subject to minor variations due to the applied raw materials and production processes.
© Gummiwerk KRAIBURG GmbH & Co. KG 01/2019KRAIBON® is protected as European Trade Mark No. 011282209. The KRAIBON® process “direct bonding of rubber with FRP” is protected by European Patent EP 1 893 405 B1, EP 2419272 B1 and further pending Patent Applications (WO 2010/118860 A1; PCT/EP2012/004106; PCT/EP2012/004041). KRAIBURG cannot guarantee that the properties above are met under all application conditions, as it has no knowledge of the actual influencing parameters.
KRAIBON®Co
mpo
und
Aco
usti
c
Impa
ct
Split
teri
ng
CFK/
Met
al-H
ybri
d
Ligh
twei
ght
Hig
h te
mpe
ratu
re
Fire
-res
ista
nce
Oil-
resi
stan
ce
AA6CFZ
AA9CFZ
AA6KFZ
AA9KFZ
UT7CFZ (SUT9609/24)
HHZ9578/99
VA6BOZ (SVA5017/41)
HAA9275/45
HVV9632/59
Very good Good
Please note that the mentioned properties and applications are only general recommendations. Contact us to find out the best possible solution for your KRAIBON®-Compound.