USULAN PROGRAM KREATIVITAS MAHASISWA
JUDUL PROGRAM
SINTESA KATALIS HETEROGEN Pt-Rh-Pd/γ-Al2O3 METODE SOL GEL UNTUK PENINGKATAN STABILITAS OKSIDASI BIODIESEL KEMIRI SUNAN
BIDANG KEGIATAN:PKM PENELITIAN
Diusulkan oleh:
Nikko Eddy Sugianto (114120002 angkatan 2012)
Dwi Ratna Mustafida (114120003 angkatan 2012)
Didit Eko Prasetyo (114130034 angkatan 2013)
Eka Fitriyani (114120035 angkatan 2013)
INSTITUT TEKNOLOGI INDONESIA
SERPONG
2014
PENGESAHAN PKM – PENELITIAN
1. Judul : Sintesa Katalis Heterogen Pt-Rh-Pd/ γ-Al2O3 Metode Sol Gel Untuk Proses Peningkatan
Stabilitas Oksidasi Biodiesel Kemiri Sunan 2. Bidang Kegiatan : PKM - P3. Ketua Pelaksana Kegiatan
a. Nama Lengkap : Nikko Eddy Sugiantob. NIM : 114120002c. Jurusan : Teknik Kimiad. Universitas/Institut/Politeknik : Institut Teknologi Indonesiae. Alamat Rumah dan No HP : JL. Raya Bumi Indah Ruko Blok RC No.26,
Bumi Indah Kelurahan Kuta jaya Kecamatan Pasar Kemis ,Tangerang. Kode Pos 15560
No.HP: 081906005036f. Alamat email : [email protected]
4. Anggota Pelaksana Kegiatan/Penulis : 3 Orang5. Dosen Pendamping
a. Nama Lengkap dan Gelar : Dr.Ir. Dwita Suastiyanti, M.Sib. NIDN : 0316096501c. Alamat Rumah dan No HP : Bukit Pamulang Indah B3 No.4 Pamulang-Ciputat
- Tangerang Selatan No.HP : 085697163727
g. Biaya Kegiatan Totala. Dikti : Rp. 12.500.000,00b. Biaya Lain : -
h. Jangka Waktu Pelaksanaa : 5 Bulan
i
ii
Tangerang Selatan, 25 September 2014
Menyetujui
Ketua Program Studi Teknik Kimia Ketua Pelaksana KegiatanInstitut Teknologi Indonesia
(Dr. Ir. Sri Handayani, MT) (Nikko Eddy Sugianto) NIDN. 0315106501 NIM 114120002
Wakil Rektor Bidang Kemahasiswaan Dosen Pendamping
( Ir. J . Victor Tuaptel, MT. PhD ) (Dr.Ir. Dwita Suastiyanti, M.Si) NIDN. 0322096803 NIDN. 0316096501
ii
DAFTAR ISI
PENGESAHAN PKM – PENELITIAN.................................................................................................................i
DAFTAR ISI.................................................................................................................................................. iii
RINGKASAN..................................................................................................................................................v
BAB I............................................................................................................................................................1
PENDAHULUAN...........................................................................................................................................1
1.1 Latar Belakang.............................................................................................................................1
1.2 Rumusan Masalah......................................................................................................................2
1.3 Tujuan Penelitian.........................................................................................................................2
1.4 Keutamaan Penelitian..................................................................................................................2
1.5 Luaran yang diharapkan...............................................................................................................2
1.6 Manfaat.......................................................................................................................................2
BAB II...........................................................................................................................................................3
TINJAUAN PUSTAKA....................................................................................................................................3
2.1 Metode Sol Gel............................................................................................................................3
2.2 Katalis..........................................................................................................................................4
2.3 Sintesis Nanopartikel γ-Al2O3.......................................................................................................4
2.4 Analisa XRD (X-Ray Diffraction)....................................................................................................6
2.5 Analisa PSA (Particle Size Analyzer) Seri Zetasizer.......................................................................6
2.6 Analisa SEM (Scanning Electron Microscopy)..............................................................................6
BAB III..........................................................................................................................................................7
METODE PENELITAN....................................................................................................................................7
3.1 Alat dan Bahan.............................................................................................................................7
3.1.1 Alat.......................................................................................................................................7
3.1.2 Bahan...................................................................................................................................7
3.2 Variabel dan Parameter...............................................................................................................7
3.2.1 Variabel................................................................................................................................7
3.2.2 Parameter............................................................................................................................7
3.3 Prosedur Percobaan....................................................................................................................7
iii
3.3.1 Cara Kerja.............................................................................................................................7
3.3.2 Analisis Sampel γ-Al2O3.......................................................................................................8
BAB IV..........................................................................................................................................................9
BIAYA DAN JADWAL KEGIATAN...................................................................................................................9
4.1 Anggaran Biaya............................................................................................................................9
4.2 Jadwal Kegiataan.........................................................................................................................9
DAFTAR PUSTAKA......................................................................................................................................10
LAMPIRAN.................................................................................................................................................11
iv
RINGKASAN
Kenaikan harga BBM secara langsung berakibat pada naiknya biaya transportasi, biaya produksi industri dan pembangkit tenaga listrik. Oleh karena itu perlu adanya energi alternatif pengganti minyak bumi salah satunya adalah biodiesel. Kemiri sunan yang banyak diperoleh di Indonesia dapat digunakan sebagai bahan dasar pembuatan biodiesel. Pembuatan biodiesel kemiri sunan melalui proses hidrogenasi parsial guna peningkatan stabilitas oksidasinya dapat dilakukan dengan menggunakan katalis heterogen (padat). Katalis heterogen mudah dipisahkan dari sistem diakhir proses atau reaksi dan dapat digunakan kembali. Disamping itu dengan menggunakan katalis heterogen tidak akan ada pembentukan sabun melalui netralisasi asam lemak bebas atau saponifikasi trigliserida. Salah satu katalis heterogen untuk proses pembentukan biodiesel adalah Pt-Rh-Pd yang disupport oleh γ-Al2O3.
γ-Al2O3 banyak tersedia dipasaran sebagai produk komersial akan tetapi diperoleh dengan harga yang mahal sehingga setelah diimpregnasi dengan Pt-Rh-Pd akan menjadi katalis yang lebih mahal lagi. Oleh karena itu dalam penelitian ini akan dicoba untuk melakukan sintesa γ-Al2O3 yang lebih ekonomis dengan metode yang lebih sederhana yaitu metode sol-gel. Dengan metode sol-gel diharapkan dihasilkan γ-Al2O3 dalam bentuk nanopartikel , fasa tunggal dan diperoleh tingkat kemurnian yang tinggi. karena γ-Al2O3 yang ada di pasaran belum tentu dalam bentuk nanopartikel dan fasa tunggal. Ukuran nano dan tidak adanya fasa impuritas menyebabkan peningkatan kinerja katalis dalam proses hidrogenasi parsial untuk meningkatkan stabilitas oksidasi biodiesel kemiri sunan. Pada proses hidrogenasi parsial ini, katalis akan mengubah asam lemak tak jenuh ganda menjadi tunggal.
Pada penelitian ini perkursor yang digunakan adalah alumunium nitrat [Al(NO3)3.9H2O] yang akan dilarutkan dalam asam sitrat. Pengadukan dilakukan diatas hotplate pada suhu 60°C selama 8 jam.Variabel yang digunakan adalah temperatur kalsinasi yaitu 450°C,550°C,650°C dan waktu kalsinasi 3 jam, 5 jam dan 7 jam. γ-Al2O3 yang telah dikalsinasi dianalisis dengan Particle Size Analyzer (PSA) metode Malvern di Dept. Fisika Universitas Indonesia , Scanning Electron Microscopy (SEM) di Dept. Metalurgi Universitas Indonesia, dan X-Ray Diffraction (XRD) di Laboratorium Material BATAN. Dan hasil analisis dibandingkan dengan γ-Al2O3 yang tersedia dipasaran.
Diharapkan dengan penelitian ini didapatkan kondisi proses optimum untuk memperoleh γ-Al2O3 nano partikel fasa tunggal dengan metode sol- gel.
Kata Kunci : katalis heterogen, biodiesel, kemiri sunan, hidrogenasi parsial.
v
1
BAB I
PENDAHULUAN
1.1 Latar BelakangKenaikan harga minyak mentah dunia akhir-akhir ini memberi dampak yang besar
pada perekonomian nasional, terutama dengan adanya kenaikan harga BBM. Kenaikan harga BBM secara langsung berakibat pada naiknya biaya transportasi, biaya produksi industri dan pembangkit tenaga listrik. Oleh karena itu perlu adanya energi alternative pengganti minyak bumi salah satunya biodiesel.
Pembuatan biodiesel umumnya dilakukan dengan menggunakan katalis basa homogen seperti NaOH dan KOH karena memiliki kemampuan katalisator yang lebih tinggi dibandingkan dengan katalis lainnya. Akan tetapi, penggunaan katalis ini memiliki kelemahan yaitu terbentuknya produk samping berupa sabun, sulit dipisahkan dari campuran reaksi sehingga tidak dapat digunakan kembali dan pada akhirnya akan ikut terbuang sebagai limbah yang dapat mencemarkan lingkungan.
Untuk mengatasi hal ini, pembuatan biodiesel dapat dilakukan dengan menggunakan katalis heterogen (padat). Katalis heterogen mudah dipisahkan dari sistem diakhir proses atau reaksi dan dapat digunakan kembali. Disamping itu dengan menggunakan katalis heterogen ini maka tidak akan ada pembentukan sabun melalui netralisasi asam lemak bebas atau saponifikasi trigliserida (Leung et al.,2009).
Pada penelitian ini akan dibuat katalis heterogen γ-Al2O3 dalam ukuran nanopartikel fasa tunggal dengan metode yang lebih mudah dan lebih ekonomis . Katalis γ-Al2O3
nanopartikel merupakan jenis material yang paling diminati karena memiliki luas area yang besar dan relative stabil pada interval temperatur pada sebagian besar reaksi katalitik. katalis γ-Al2O3 pada umumnya dapat diperoleh dipasaran akan tetapi harganya cukup mahal dan terkadang material dalam bentuk konvensional tersebut tidak cukup efektif, salah satunya disebabkan oleh aktivitas katalis yang rendah sehingga tidak mampu merengkah reaktan menjadi fraksi-fraksi bakar konvensional. Selain itu aktivitas katalis dibatasi oleh pembentukan kokas dan pori-pori katalis tertutup oleh kokas (Setiadi dkk.,2006).
Salah satu cara untuk meningkatkan kinerja katalis adalah membuat ukurannya menjadi nanopartikel. Penggunaan katalis nanopartikel telah diteliti oleh sarrano,dkk menggunakan katalis ZSM-5 dalam perengkahan LDPE (Low Density Polyethilen). Hasil yang didapat menunjukkan bahwa nanopartikel ZSM-5 memiliki aktivitas katalis yang lebih tinggi daripada mikropartikel. Oleh sebab itu dalam penelitian ini ukuran katalis γ-Al2O3 akan dibuat ukuran nanopartikel.
Metode yang digunakan dalam penelitian ini adalah metode sol gel karena metode ini memiliki banyak kelebihan diantaranya proses berlangsung pada temperatur rendah,
2
prosesnya relatif lebih mudah, bisa diaplikasikan dalam segala kondisi (versatile), menghasilkan produk dengan kemurnian dan kehomogenan yang tinggi jika parameternya divariasikan. Selain itu, yang paling mengesankan dari proses sol-gel adalah biayanya relatif murah dan produk berupa xerogel silika yang dihasilkan tidak beracun (Zawrah et al, 2009).
1.2 Rumusan Masalahγ-Al2O3 banyak tersedia dipasaran sebagai produk komersial tetapi diperoleh dengan
harga yang mahal sehingga setelah diimpregnasi dengan Pt-Rh-Pd akan menjadi katalis yang lebih mahal lagi. Oleh karena itu dalam penelitian ini akan dicoba untuk melakukan sintesa γ-Al2O3 yang lebih ekonomis dengan metode yang lebih sederhana. Dengan metode ini diharapkan dihasilkan γ-Al2O3 dalam bentuk nanopartikel dan fasa tunggal karena γ-Al2O3 yang ada dipasaran belum tentu dalam bentuk nanopartikel dan fasa tunggal.
1.3 Tujuan PenelitianTujuan penelitian ini adalah Sintesa Sintesa Katalis Heterogen Pt-Rh-Pd/ γ-Al2O3
Metode Sol Gel Untuk Proses Peningkatan Stabilitas Oksidasi Biodiesel Kemiri Sunan
1.4 Keutamaan PenelitianKeutamaan penelitian ini adalah akan diperoleh katalis γ-Al2O3 dengan metode yang
lebih efisien dan ekonomis sehingga dapat mengurangi biaya produksi, serta dapat diaplikasikan ke industri-industri katalis.
1.5 Luaran yang diharapkanDengan melakukan penelitian ini, diharapkan dapat dihasilkan kondisi optimum
untuk menghasilkan γ-Al2O3 nano partikel fasa tunggal dengan metode sol gel , serta diharapkan dapat dijadikan karya ilmiah untuk jurnal nasional, seminar nasional dan jurnal IPTEK Institut Teknologi Indonesia ber-ISSN.
1.6 ManfaatManfaat dari penelitian ini adalah sebagai metode pembuatan katalis dengan metode
sol gel yang lebih ekonomis dan efisien , serta untuk mendukung sumber energi nasional.
3
BAB II
TINJAUAN PUSTAKA
2.1 Metode Sol GelMetode sol gel dapat didefinisikan sebagai proses pembentukan senyawa
anorganik melalui reaksi kimia dalam larutan pada suhu rendah, dimana dalam proses tersebut terjadi perubahan fasa dari suspensi koloid (sol) membentuk fasa cair kontinyu (gel). Bahan awal dalam pembuatannya adalah alkoksida logam dan klorida logam, yang kemudian mengalami reaksi hidrolisis dan reaksi polikondensasi untuk membentuk koloid, yaitu suatu sistem yang terdiri dari partikel-partikel padat (ukuran partikel antara 1 nm sampai 1 µm) yang terdispersi dalam suatu pelarut (Hench & West, 1990).
Reaksi Sol Gel
Ada dua tahapan reaksi dalam Sol Gel
1. Hidrolisis metal alkoksida
2. Kondensasi
Menurut Iler, polimerisasi sol-gel terjadi dalam tiga tahap:
1. Polimersasi monomer-monomer membentuk partikel
2. Penumbuhan partikel
4
3. Pengikatan partikel membentuk rantai, kemudian jaringan yang terbentuk diperpanjang dalam medium
Keuntungan menggunakan metoda Sol Gel
Homogenitasnya lebih baik, Temperatur rendah, Kemurnian lebih baik, Hemat energy, Pencemaran rendah, Menghindari reaksi dengan container dan kemurnian tinggi. Fase pemisahan cepat, Kristalisasi cepat, Padatan non kristalin keluar membentuk gelas Pembentukan fase kristal baru dari padatan non kristal baru.
Kerugian menggunakan metoda Sol Gel
Material proses cukup mahal, Residu butir-butir halus, Residu hidroksil Residu carbon, Waktu proses cukup lama ( J.D.Mackenzie, J.Non-Cryst.Solids,48, 1 (1982) )
2.2 Katalis Katalis merupakan suatu bahan yang dapat meningkatkan laju suatu reaksi kimia
dalam mencapai keadaan kesetimbangan tanpa terlibat secara permanen didalam suatu reaksi. Katalis terbagi menjadi dua yaitu katalis homogen dan heterogen
Katalis Homogen Katalis homogen sulit dipisahkan dari campuran reaksi sehingga tidak
dapat digunakan kembali dan pada akhirnya akan ikut terbuang sebagai limbah yang dapat mencemarkan lingkungan.
Katalis Heterogen Katalis berupa padatan dan reaktan serta produk berupa fasa cair atau gas.
jenis katalis ini lebih banyak digunakan karena lebih murah, mudah dipisahkan dari reaktan serta sangat mudah beradaptasi dengan berbagai reaktor.
Alumina untuk penggunaan sebagai katalis adalah alumina transisi. γ-Al2O3 adalah material yang paling diminati karena memiliki luas area yang besar dan relative stabil pada interval temperature pada sebagian besar reaksi katalitik. Dahulu α-Al2O3 juga diminati karena memiliki keasaman yang lebih tinggi daripada γ-Al2O3 sehingga dapat menjadi support yang sangat berguna untuk reaksi catalytic reforming.
2.3 Sintesis Nanopartikel γ-Al2O3
Sampai saat ini nanopartikel Al2O3 dapat disintesis oleh berbagai metode, seperti co-precipitation, sol-gel, dan thermal decomposition. Co-precipitation dan metode sol-gel yang digunakan untuk menyiapkan oksida logam atau oksida logam komposit dengan reaksi kimia.
5
Banyak studi penelitian yang telah dilakukan dengan menghasilkan γ-Al2O3 berukuran nanometer berdasarkan dari fase cair, sintesis fasa gas atau perlakuan hidrotermal pada tekanan tinggi. Tetapi metode – metode tersebut tidak ada yang cocok untuk mengontrol sifat dari γ-Al2O3. Metode sol – gel adalah yang paling menjanjikan untuk mempersiapkan serbuk γ-Al2O3 dengan kemurnian sangat tinggi dan dengan area permukaan yang tinggi. Teknik sintesis alumina dengan sol – gel umumnya menghasilkan campuran fase alumina (θ, γ dan δ) dan mengubah ke fase α-Al2O3 dengan pemanasan pada suhu tinggi. Macedo et al.,2004, mengatakan bahwa sintesis γ-Al2O3 dengan metode sol – gel dari larutan jenuh aluminium nitrat menggunakan urea sebagai penetral dan sebagai agen pengkontrol hidrolisis.
Luas permukaan alumina tergantung pada tingkat agregasi dan terputusnya butiran alumina gel selama proses aging, yang sangat dipengaruhi oleh pH presipitasi. Dalam hubungan ini, teramati bahwa pH asam (pH = 6), agregasi butiran alumina gel mungkin terbentuk, yang mengarah ke formasi oksida dengan pori-pori yang lebih kecil dan luas permukaan yang tinggi, sementara pada pH (pH =7-8) yang lebih tinggi terputusnya butiran gel alumina terbentuk, menghasilkan pembentukan oksida dengan pori-pori yang lebih besardan lebih rendah luas permukaan (Yvan J.O.Asencios et al, 2012.). Okada et al, Panias and Krestou., hubungan korelasi pH presipitasi gel dengan ukuran Kristal alumina terbentuk.
Beberapa hasil penelitian dalam sintesis γ-Al2O3 :
1. Potdar et al., diperoleh γ-Al2O3 dari boehmite (disintesisdari Al(NO3)3 dan Na2CO3, pada pH sedikit basa, dan berusia di 70 oC selama 3 jam); luas permukaan maksimum alumina yang 258 m2 g-1.
2. Kim et al., juga memproduksi γ-Al2O3 dari boehmite (disintesis dari isopropoxide aluminium, asam asetat dan isopropanol pada pH sedikit asam, dan usia pada 80 oC selama 20 jam); permukaan maksimum daerah mencapai sebesar 307 m2 g-1.
3. Meephoka et al., mensintesis γ-Al2O3 dari larutan campuran toluena dan 1-butanol dalam aluminium isopropoxide (penuaan dalam sistem autoclave pada 300 oC dengan adanya N2, dan dikalsinasi pada 600 oC), luas permukaan maksimum adalah 226 m2 g-1.
4. Guzman-Castillo et al., menyiapkan boehmite dari solusi Al2(SO4)3.18H2O, AlCl3
dan NH4OH pada pH 7-9 (berusia di 50, 140 dan 180 oC selama 18 jam), luas permukaan maksimum alumina adalah 248 m2 g-1.
5. Rahmanpour et al.2012., γ-Al2O3 disintesis dari Al(NO3)3-9H2O (0.26M), NH4OH (3.2%), dan air deionized pada pH 7.5-8.5 dengan suhu 310 hingga 340 oC selama 15 jam dan konversi methanol 84%. Menghasilkan ukuran Kristal 1-2 nm, luas permukaan 216 m2/g, rata-rata pori diameter 9.646 nm, dan volume pori 0.5212 cm3/g.
6
6. Arquimede et al.2008., mensintesis serbuk nano γ-Al2O3 dengan menggunakan tiga jenis asam (asam sulfat, asam nitrat, dan asam sitrat) pada suhu 600 oC. Dengan hasil untuk luas permukaan 347 m2g-1 (nitric acid), 252 m2g-1 (acetic acid), 164 m2g-1
(citric acid) ; untuk ukuran pori 8 nm (nitric acid), 3 nm (acetic acid), 9 nm (citric acid) ; untuk volume pori 0.50 cm3g-1
(nitric acid), 0.97 cm3g-1 (acetic acid), 0.72 cm3g-1 (citric acid).
2.4 Analisa XRD (X-Ray Diffraction)Karakteristik XRD (X-Ray Diffraction) dapat digunakan untuk menentukan struktur
kristal menggunakan sinar-X. Metode ini dapat digunakan untuk menentukan jenis struktur, ukuran butir, konstanta kisi (smallman and bishop, 1999).
2.5 Analisa PSA (Particle Size Analyzer) Seri ZetasizerParticle Size Analyzer (PSA) seri zetasizer (Malvern) paling banyak digunakan untuk
pengukuran nanopartikel, koloid, dan protein, zeta potensial, dan bobot molekul. alat ini mampu mengukur ukuran partikel dan molekul yang berada dalam rentang 0,15 nm sampai 10 µm.
2.6 Analisa SEM (Scanning Electron Microscopy)Scanning Electron Microscopys (SEM) adalah sebuah instrumen berkekuatan besar
dan sangat handal yang dipadukan dengan EDX (Energy Dispersive X-Ray Spectroscopy) sehingga dapat digunakan untuk memeriksa, observasi, dan karakterisasi struktur terkecil benda-benda padat dari material organik maupun anorganik yang heterogen serta permukaan bahan dengan skala micrometer (Kroschwitz, 1990).
7
BAB III
METODE PENELITAN
3.1 Alat dan Bahan
3.1.1 Alat
Alat yang digunakan : seperangkat alat XRD (X-ray Diffraction), SEM (Scanning Electron Microsopy), PSA (Particle Size Analyzer) Metode Malvern, Refluks, Magnetic Stirer, Oven.
3.1.2 Bahan
Bahan yang digunakan : Aquadest, Alumunium nitrat [Al(NO3)3.9H2O] ( 99,99%, Merck, Amonium hidroksida (NH4OH) dari Merck dengan analytical grade, Asam
sitrat, Pt-Rh-Pd/γ-Al2O3 komersil
3.2 Variabel dan Parameter
3.2.1 Variabel
Temperatur kalsinasi 450°C, 550°C, 650°C Waktu kalsinasi 3 jam, 5 jam dan 7 jam
3.2.2 Parameter
Parameter yang diukur :
Ukuran partikel γ-Al2O3 setelah kalsinasi dengan Particle Size Analyzer (PSA)
3.3 Prosedur Percobaan
3.3.1 Cara Kerja
Disiapkan larutan alumunium nitrat [Al(NO3)3.9H2O] dan asam sitrat dengan perbandingan 1 : 2
Ditambahkan ammonium hidroksida (NH4OH) sedikit demi sedikit agar pH berubah menjadi ±7,5
Diaduk secara kontinyu selama 8 jam diatas hotplate dan dijaga suhunya 60°C, dilakukan di Laboratorium Kimia Institut Teknologi Indonesia
8
3.3.2 Analisis Sampel γ-Al2O3
Analisis γ-Al2O3 komersial, dilakukan uji Scanning Electron Microscopy (SEM) di Dept. Metalurgi Universitas Indonesia dan X-Ray Diffraction (XRD) di Laboratorium Material BATAN.
Analisis ukuran γ-Al2O3 terkalsinasi dilakukan uji Particle Size Analyzer (PSA) metode Malvern di Dept. Fisika Universitas Indonesia , Scanning Electron Microscopy (SEM) di Dept. Metalurgi Universitas Indonesia, dan penentuan struktur Kristal γ-Al2O3 terkalsinasi dilakukan uji X-Ray Diffraction (XRD) di Laboratorium Material BATAN.
3.4 Matrik PenelitianSuhu
Kalsinasi (oC)
Waktu Kalsinasi
(JAM)
UjiXRD
UjiPSA
UjiSEM
450357
550357
650357
Dikalsinasi pada suhu 450°C, 550°C, 650°C selama 3,5 dan 7 jam
Dibakar pada temperature 400°C
Dikeringkan pada suhu 90°C
9
BAB IV
BIAYA DAN JADWAL KEGIATAN
4.1 Anggaran Biaya
No Jenis Pengeluaran Biaya (Rp)1 Peralatan Penunjang 3.125.0002 Bahan Habis Pakai 4.375.0003 Perjalanan 3.125.0004 Lain-lain: administrasi, publikasi, seminar, laporan, lainnya 1.875.000
Jumlah 12.500.000
4.2 Jadwal Kegiataan
No
Kegiatan
Bulan
Ke-1 Ke-2 Ke-3 Ke-4 Ke-5
1 2 3 4 1 2 3 4 1 2 3 4 1 2 3 4 1 2 3 4
1Pemahaman konsep dan
teori
2Persiapan Alat
dan Bahan
3
4
5Pengumpulan dan Analisis
Data
6Pembuatan
Laporan
10
DAFTAR PUSTAKA
Asencios, Y.J.O.,Sun-Kou M.R.Synthesis of high-surface-area γ-Al2O3 from aluminum scrap and its use for the adsorption of metal : Pb(II), Cd(II), Zn(II). Applied Surface Science 258 (2012) 10002-10011
Cruz-Lopez, A.,dkk.Synthesis of γ-Al2O3 nanopowder by the sol-gel method: Effect of different acid precursors on the superficial,morphological and structural properties, journal of ceramic processing, vol. 9, No. 5, pp. 474-477(2008)
Karim M.R.,dkk.Synthesis of γ-Al2O3 Particles and Surface Characterization.The Open Colloid Science Journal,2011,4,32-36
Ke-Long ,Huang ,dkk.2006.Preparation and formation mechanism of Al2O3 nanoparticles by reverse microemulsion,Trans. Nonferrous Met.Soc.China 17(2007) 633-637
Leung,Dannis Y.C.,Xuan Wu, M.K.H. Leung ,2009. A Review on Biodiesel Production Using catalyzed Transesterification. Applied Energy 87 (2010) 1083-1095
Nugroho, Agung,dkk.2014. Preparasi Katalis Heterogen Berbasis Abu Kiln Semen Untuk Produksi Biodiesel.Proposal PKM-P
Rahmanpour O.,dkk.2012. New Method For Synthesis Nano Size γ-Al2O3 Catalyst for Dehydration of Methanol to Dimethyl Ether.International Journal of Chemical Engineering and Applications, Vol. 3, No. 2, April 2012
Rogojan, Radica,dkk. Synthesis and Characterization of Alumina Nano-Powder Obtained By Sol-Gel Method. U.P.B. Sci. Bull., Series B, Vol. 73, Iss. 2,2011
Setiadi, Mailisa , F.,(2006).Proses Katalitik Sintesis Hidrokarbon Fraksi Bensin Dari Minyak Sawit Menggunakan Katalis B2O3/Zeolit .Seminar Nasional MKICS,Universitas Indonesia,94-98
Sinaga, A.C.2011.Preparasi,Karakterisasi dan Uji Reaksi Katalis Nano NiO/Al2O3 untuk Sintesis Bahan Bakar Bio Non Ester dari Minyak Jarak Melalui Pirolisis Berkatalis. Skripsi FT UI
Widodo,Slamet. Teknologi Sol Gel Pada Pembuatan Nano Kristalin Metal Oksida Untuk Aplikasi Sensor Gas, Seminar Rekayasa Kimia Dan Proses 2010 ISSN : 1411-4216
Zawrah, M. F., El-Kheshen, A. A., Abd-El-All, H., Facile and Economic Synthesis of Silica Nanoparticles, Journal of Ovonic Reasearch, vol.5, No.5, 2009, pp.129-133
11
LAMPIRAN
Lampiran 1. Biodata Ketua, Anggota dan Dosen PembimbingBiodata Ketua Pelaksana
A. Identitas Diri Anggota1 Nama Lengkap Nikko Edy Sugianto2 Jenis Kelamin Laki-laki3 Program Studi Teknik Kimia4 NIM 114 12 00025 Tempat dan Tanggal Lahir Tangerang, 23 Januari 19946 E-mail [email protected] No HP 081906005036
B. Riwayat PendidikanSD SMP SMA
Nama Institusi SD Kusuma Bangsa II
SMP Dharma Putra SMA Dharma Putra
Jurusan - - IPATahun Masuk-Lulus 2000 – 2006 2006 – 2009 2009 – 20012
C. Pemakalah Seminar Ilmiah (oral presentation)No Nama Pertemuan Ilmiah Judul Artikel Ilmiah Waktu dan
Tempat1 - - -2 - - -3 - - -
D. Penghargaan dalam 10 Tahun Terakhir (dari pemerintah, asosiasi atau institusi lainnya)
No Jenis Penghargaan Institut Pemberi Penghargaan Tahun1 Sertifikat Seminar
Nasional“Energi Baru dan Terbarukan Coal Bed Methane
dan Geothermal”
Kementrian Perindustrian 2013
2 Sertifikat Chemistry Fair “Rising Youth Innovation For Renewable
Energy”
Universitas Indonesia 2013
12
3 Sertifikat Seminar – Workshop Series Gas “Optimizing Gas Production and Processing”
Universitas Indonesia 2014
Semua data yang saya isikan dan tercantum dalam biodata ini adalah benar dan dapat dipertanggungjawabkan secara hukum. Apabila di kemudian hari ternyata dijumpai ketidaksesuaian dengan kenyataan, saya sanggup menerima sanksi.Demikian biodata ini saya buat dengan sebenarnya untuk memenuhi salah satu persyaratandalam pengajuan Hibah PKM-P.
Tangerang Selatan, 25 September 2014Pengusul
Nikko Eddy Sugianto
13
Biodata Anggota 1
A. Identitas Diri Anggota1 Nama Lengkap Dwi Ratna Mustafida2 Jenis Kelamin Perempuan3 Program Studi Teknik Kimia4 NIM 114 12 00035 Tempat dan Tanggal Lahir Malang,25 Januari 19936 E-mail [email protected]
7 No HP 089683119650
B. Riwayat PendidikanSD SMP SMA
Nama Institusi MI Nurul Huda 01Malang
SMPN 1 Tumpang-Malang
SMAN 3 Cilegon
Jurusan - - IPATahun Masuk-Lulus 2000-2006 2006-2009 2009-2012
C. Pemakalah Seminar Ilmiah (oral presentation)No Nama Pertemuan Ilmiah Judul Artikel Ilmiah Waktu dan
Tempat1 - - -2 - - -3 - - -
D. Penghargaan dalam 10 Tahun Terakhir (dari pemerintah, asosiasi atau institusi lainnya)
No Jenis Penghargaan Institut Pemberi Penghargaan Tahun1 Sertifikat Seminar Nasional“Energi
Baru dan Terbarukan Coal Bed Methane dan Geothermal”
Kementrian Perindustrian 2013
2 Sertifikat Chemistry Fair “Rising Youth Innovation For Renewable Energy”
Universitas Indonesia 2013
3 Sertifikat Seminar – Workshop Series Gas “Optimizing Gas Production and Processing”
Universitas Indonesia 2014
Semua data yang saya isikan dan tercantum dalam biodata ini adalah benar dan dapat
14
dipertanggungjawabkan secara hukum. Apabila di kemudian hari ternyata dijumpai ketidaksesuaian dengan kenyataan, saya sanggup menerima sanksi.Demikian biodata ini saya buat dengan sebenarnya untuk memenuhi salah satu persyaratandalam pengajuan Hibah PKM-P.
Tangerang Selatan, 25 September 2014Pengusul
Dwi Ratna Mustafida
15
Biodata Anggota 2
E. Identitas Diri Anggota1 Nama Lengkap Didit Eko Prasetyo2 Jenis Kelamin Laki Laki3 Program Studi Teknik Kimia4 NIM 1141300345 Tempat dan Tanggal Lahir Jakarta, 14 Desember 19956 E-mail [email protected] No HP 08988786996
F. Riwayat PendidikanSD SMP SMA
Nama Institusi SDN Setu 1 SMPN 1 Tangsel
SMAN 07 Tangsel
Jurusan - - IPATahun Masuk-Lulus 2001-2007 2007-2010 2010-2013
G. Pemakalah Seminar Ilmiah (oral presentation)No Nama Pertemuan Ilmiah Judul Artikel Ilmiah Waktu dan
Tempat1 - - -2 - - -3 - - -
H. Penghargaan dalam 10 Tahun Terakhir (dari pemerintah, asosiasi atau institusi lainnya)
No Jenis Penghargaan Institut Pemberi Penghargaan Tahun1 Sertifikat Peserta Kegiatan
Penyisihan Tingkat Provinsi Lomba Cerdas Cermat 4(Empat) Pilar Kehidupan, Berbangsa dan Bernegara
Majelis Permusyawaratan Rakyat Repubik Indonesia
2012
2 Sertifikat Konferensi Nanoteknologi Pelajar Nasional
Universitas Indonesia 2013
3 Sertifikat seminar dan diskusi nasional ADVANCING INDONESIA’S ENERGY WITH GEOPHYSICS
Universitas Indonesia 2014
Semua data yang saya isikan dan tercantum dalam biodata ini adalah benar dan dapat
16
dipertanggungjawabkan secara hukum. Apabila di kemudian hari ternyata dijumpai ketidaksesuaian dengan kenyataan, saya sanggup menerima sanksi.Demikian biodata ini saya buat dengan sebenarnya untuk memenuhi salah satu persyaratandalam pengajuan Hibah PKM-P.
Tangerang Selatan, 25 September 2014Pengusul
Didit Eko Prasetyo
17
Biodata Anggota 3
I. Identitas Diri Anggota1 Nama Lengkap Eka Fitriyani2 Jenis Kelamin Perempuan3 Program Studi Teknik Kimia4 NIM 1141300355 Tempat dan Tanggal Lahir Jakarta, 3 Maret 19956 E-mail [email protected] No HP 085781796838
J. Riwayat PendidikanSD SMP SMA
Nama Institusi SDI ASSA’ADAH Jakarta SMPN 37 Jakarta
SMA Bakti Idhata Jakarta
Jurusan Umum/Reguler Umum/Reguler IPATahun Masuk-Lulus 2001-2007 2007-2010 2010-2013
K. Pemakalah Seminar Ilmiah (oral presentation)No Nama Pertemuan Ilmiah Judul Artikel Ilmiah Waktu dan
Tempat1 Seminar Chemical
EngineeringMengenai Limbah, Material dan Energi
13/09/2013 di Institut Teknologi Indonesia
2 Seminar Mengenai Busa Mengenai Pembuatan dan Pengolahan Busa untuk Berbagai Kegunaan
Di Institut Teknologi Indonesia
3 - - -
L. Penghargaan dalam 10 Tahun Terakhir (dari pemerintah, asosiasi atau institusi lainnya)
No Jenis Penghargaan Institut Pemberi Penghargaan Tahun1 Ikut dalam Olimpiade Kimia SMA Bakti Idhata Jakarta 20122 Ikut dalam Lomba Karya Ilmiah Kementrian Pendidikan dan
Kebudayaan2012
3 - - -
Semua data yang saya isikan dan tercantum dalam biodata ini adalah benar dan dapatdipertanggungjawabkan secara hukum. Apabila di kemudian hari ternyata dijumpai ketidaksesuaian dengan kenyataan, saya sanggup menerima sanksi.Demikian biodata ini saya buat dengan sebenarnya untuk memenuhi salah satu persyaratandalam pengajuan Hibah PKM-P.
18
Tangerang Selatan, 25 September 2014Pengusul
Eka Fitriyani
19
Biodata Dosen Pembimbing
M. Identitas Diri1 Nama Lengkap Dr.Ir. Dwita Suastiyanti M.Si L/P2 Jabatan Fungsional Lektor Kepala (711,50 kum) TMT 31/08/20063 Jabatan Struktural -------------------4 Pangkat Penyetaraan, golongan
ruang, tmtPembina, golongan ruang IVA, tmt 1 Januari 2014
5 Nomor Sertifikat Pendidik 081612094946 NIDN 03160965017 Tempat dan Tanggal Lahir Bandung, 16 September 19658 Alamat Rumah Bukit Pamulang Indah B3 No.4 Pamulang-
Ciputat - Tangerang Selatan9 Nomor Telepon/Faks/HP (021) 7425761 / ----- / 08569716372710 Alamat Kantor Jl. Raya Puspiptek - Serpong11 Nomor Telepon / Faks (021) 7561091 / ------12 Alamat Email [email protected]
[email protected] Lulusan Yang Telah Dihasilkan S-1 = 215 orang S-2 = -- orang S-3 = ---- orang
14. Mata Kuliah Yang Diampu
1. Material Teknik2. Proses Produksi3. Metalurgi fisik4. Pemilihan Bahan & Proses5. Korosi dan Pencegahannya
N. Riwayat PendidikanS-1 S-2 S-3
Nama Perguruan Tinggi Universitas Indonesia
Universitas Indonesia
Universitas Indonesia
Bidang Ilmu Teknik Metalurgi Ilmu Material Ilmu MaterialTahun Masuk – Lulus 1984 - 1989 1993 - 1995 2010 - 2014JudulSkripsi/Thesis/Disertasi Pengaruh %
Reduksi Cold Roll Pada Lembaran Baja Karbon Rendah
Efek Strain Aging pada Logam Aluminium Untuk Komponen Pesawat Terbang
Sintesa Material Nanokomposit Berbasis BaTiO3
dan BaFe12O19
dengan Metode Sol-Gel untuk Aplikasi Material
20
MultiferroicNama Pembimbing/Promotor Ir. Sriati Djaprie
MMetDr. Bambang Soegijono
Dr. Bambang Soegijono
O. Pengalaman Penelitian Dalam 5 Tahun Terakhir
No Tahun Judul PenelitianPendanaan
Sumber Jml (Juta Rp)1 2007 Pengaruh Dimensi
Cetakan dan Kecepatan Putar Roll Terhadap Kekerasan dan Struktur Mikro Pada Proses Pembuatan Lembaran Aluminium dengan Proses Melt Drag
Kerja sama ITI-BPPT 15
2 2008 Pengaruh Temperatur Pemanasan Pada Hasil Proses Pengecoran Pembentukan Slab Kuningan Terhadap Struktur Mikro dan Kekerasannya
Kerja sama ITI- BPPT 15
3 2009 Pengaruh Pengerolan Dingin dan Penambahan Unsur Aluminium Terhadap Struktur Mikro dan Kekerasan Lembaran Kuningan
Kerja sama ITI- BPPT 15
4 2009 Pengaruh Posisi Cetakan Logam Pada Proses Pengecoran Untuk Pembentukan Slab Kuningan Terhadap Struktur Mikro dan Kekerasannya
Hibah Penelitian Dosen Muda dan Studi Kajian Wanita
10
5 2010 Pengaruh Temperatur Kalsinasi Pada Proses Sol Gel Auto Combustion Terhadap Sifat-Sifat Fisis Material Feromagnetik
Grant DRPM UI, No. Kontrak3423/H2.R12/PPM 00.01,2010
200
21
dan Ferroelektrik.6 2011 Pergeseran Pola Difraksi
Sinar – X Pada Material Feromagnetik dan Feroelektrik.
Grant DRPM UI, No. Kontrak3423/H2.R12/PPM 00.01,2011.
200
7 2011 Proses Sol Gel Auto Combustion Pada Sintesa Material Ferroic
Grant DRPM UI, No. Kontrak3423/H2.R12/PPM 00.01,2011.
200
8 2012 Pengaruh Temperatur Sinter dan pada Proses Sol-Gel Auto Combustion Terhadap Ukuran Partikel Material Ferroic
Mandiri
25
9 2013 Proses Sol-Gel Auto Combustion pada Sintesa Material BiFeO3
Insentif Riset SiNas No 26/SEK/INSINAS/PPK/I tahun 2013 280
10 2013 Karakterisasi Elektrik dan Magnetik pada Material Nanokomposit Multiferroic
Insentif Riset SiNas No 26/SEK/INSINAS/PPK/I tahun 2013 280
10 2013 Rekayasa Material Elektrik BaTiO3 dan Pengembangannya Menjadi Material Ferroic Nanokomposit Sistem Bulk untuk Aplikasi Sensor
Hibah Desentralisasi Dikti (Penelitian Disertasi Doktor) No. 025/K3.KM/2013, Kopertis 3, DIKTI
44
11 2014 Sintesa Material Multiferroic Sistem Multilayer Berbasis BaTiO3 dan BaFe12O19
Insentif Riset SiNas No 17/SEK/INSINAS/PPK/I tahun 2014
250
12 2014 Sintesa Material Multiferroic BiFeO3
Metode Spin Coating
Insentif Riset SiNas No 17/SEK/INSINAS/PPK/I tahun 2014
250
13 2014 Eksplorasi Eksperimental Sintesa BaTiO3 Metode Sol-gel dan Pengembangannya pada Rekayasa Material
Hibah Desentralisasi Dikti (Penelitian Fundamental) tahun 2014/Tahun INo. 209/K3/KM/2014, Kopertis 3,
71,5
22
Multiferroic Nanokomposit (Bulk) untuk Aplikasi Smart Sensor
DIKTI,Kemendikbud
P. Pengalaman Pengabdian Kepada Masyarakat Dalam 5 Tahun Terakhir
No Tahun Judul Pengabdian Kepada MasyarakatPendanaan
Sumber Jml (Juta Rp)1 2009-2010 “Study on Investment Mapping for
the Development of Chemicals Industry and Its Derivates In the Leverage of Competitive-ness”.
Badan Koordinasi Penanaman Modal (BKPM) -PT.Sucofindo
2 2009-2010 “Masterplan Arah Pengembangan dan Pemetaan Investasi Industri Manufaktur Bagi 6 Sektor Industri (makanan minuman, Pulp & Paper, Logam Dasar, Petrokimia , Otomotif dan Kimia Dasar , Garam dan Oleokimia berbasis Kelapa Sawit)”.
Badan Koordinasi Penanaman Modal (BKPM) -PT.Sucofindo
3 2010-2011 ”Pengembangan Industri Bahan Kimia Khusus Berbasis Hasil Samping dan atau Limbah Industri CPO dan turunannya”.
Industri Kimia Hulu, Direktorat Jenderal Industri Argo dan Kimia Kementerian Perindustrian – PT. Sucofindo
4 2011-2012 “Pengembangan Keterampilan Soft Skill dan Hard Skill Bidang Otomotif Santri Pondok Pesantren Tremas Pacitan Jawa Timur”
Direktorat Pendidikan Diniyah dan Pondok Pesantren, Kementerian Agama RI.
5 2014 Moderator Pelatihan Penulisan Artikel Ilmiah pada Jurnal Terakreditasi
Lembaga Penelitian, Pengabdian
23
dan Pemberdayaan Masyarakat, ITI, 5 Maret 2014
6 2014 Anggota Tim Pembina Intel International Science and Engineering Fair (INTEL-ISEF) 2014, Siswa-siswa SMAN 2 Sekayu, Sumatera Selatan (Green Refrigerant Box)
Kementerian Pendidikan dan Kebudayaan, Direktorat Jenderal Pendidikan Menengah , Direktorat Pembinaan Sekolah Menengah Atas
7 2014(Juni-Agustus)
Ketua Kajian Desk Research untuk Komoditi Timah Sebagai Subyek Sistem Resi Gudang (SRG)
Bappebti (Badan Pengawas Perdagangan Berjangka Komoditi, Kementerian Perdagangan Republik Indonesia
8 2014-2016 Anggota Tim Penanganan Perguruan Tinggi Bermasalah
Dirjen Dikti, Kementerian Pendidikan dan Kebudayaan, Republik Indonesia
9 Agustus s/d Desember 2014
Tim Pembina OPSI (Olimpiade Penelitian Siswa Indonesia) 2014, Siswa-siswa SMAN 2 Sekayu, Sumatera Selatan (Thrombe Wall)
Kementerian Pendidikan dan Kebudayaan, Direktorat
24
Jenderal Pendidikan Menengah , Direktorat Pembinaan Sekolah Menengah Atas
Q. Pengalaman Penulisan Artikel Ilmiah Dalam Jurnal Dalam 5 Tahun TerakhirNo Judul Artikel Ilmiah Volume/Nomor/Tahun Nama Jurnal1 Casting and Cold Rolled
Process of Brass Sheet As A Radiator Material
Proceeding of The International Conference on Materials Science and Technology ICMST 2010
2 Influence of Ba/Fe Mole Ratios on Magnetic Properties, Crystallite Size and Shifting of X-Ray Diffraction Peaks of Nanocrystalline BaFe12O19
Powder Prepared by Sol-Gel Auto Combustion
Citation: AIP.Conf.Proc, 1454,238, 2012
AIP (American Institute of Physics) Conference Proceeding
3 Pengaruh Pergeseran Puncak Difraksi Akibat Perubahan Rasio Mol Ba2+/Fe3+ Terhadap Sifat Magnetik BaFe12O19 Sol-Gel
Volume 8 No.2, Juli 2012
Jurnal Pendidikan Fisika Indonesia (JPFI) Terakreditasi No.81/DIKTI/Kep/2011, ISSN 1693-1246
4 Shifting of X-Ray Diffraction Pattern Peak on BaFe12O19
Nanocrystalline Produced by Sol-Gel Auto Combustion Method
Volume 576, pp 240-243, 2012
Advanced Materials Research Journal, Trans.Tech.Publication, Switzerland.
5 Nanosize Effects on Magnetic Properties and Peak Shifting of X-Ray Diffraction Pattern of BaFe12O19 Produced by Sol-Gel Method.
Vol. 789 , pp 87-92, 2013
Advanced Materials Research Journal, Trans.Tech.Publication, Switzerland.
6 Magnetic Behaviors of Nanocomposite Based on
Vol. 789 pp 118-123, 2013
Advanced Materials Research Journal,
25
Differences in Volume Fraction Prepared by Sol-Gel.
Trans.Tech.Publication, Switzerland.
7 Simple Recipe to Synthesize BaTiO3-BaFe12O19
Nanocomposite Bulk System With High Magnetization
Vol. 493 pp 634-639, 2014
Applied Mechanics and Materials Journal, Trans. Tech. Publication, Switzerland.
8 Magnetoelectric Coupling Phenomena Based on The Changes of Magnetic Properties in Multiferroic NanocompositeBaTiO3-BaFe12O19 System
Vol. 896 pp 385-390, 2014
Advanced Materials Research Journal, Trans.Tech.Publication, Switzerland.
9 The Influence of BTO-BHF Different Composition on its Ferroelectric Properties
Volume 495 (2014) 012007
Journal of Physics(Second Author)
10 Rekayasa Material Komposit Multiferroic Nanopartikel Berbasis Barium Hexaferrite-Barium Titanate dengan Metode Sol-Gel untuk Aplikasi Sensor
Tahun 2013 Proceeding Seminar Nasional Insentif Riset SINas 2013
11 Karakteristik Elektrik Nanopartikel BaTiO3 untuk Aplikasi Material Multiferroic
Volume 5, No. 1, 21 Juni 2014
Prosiding Seminar Nasional Sains dan Pendidikan Sains IX, ISSN 2087-0922
R. Pengalaman Penyampaian Makalah Secara Oral Pada Pertemuan / Seminar Ilmiah Dalam 5 Tahun Terakhir
No Nama Pertemuan Ilmiah / Seminar Judul Artikel Ilmiah Waktu dan Tempat1 Seminar Hasil Penelitian Dosen Muda
dan Studi Kajian WanitaPengaruh Posisi Cetakan Logam Pada Proses Pengecoran Untuk Pembentukan Slab Kuningan Terhadap Struktur Mikro dan Kekerasannya
2009, Jakarta
2 International Conference on Materials Science and Technology ICMST 2010”
Casting and Cold Rolled Process of Brass Sheet as A
2010, BATAN Serpong
26
Radiator Material.3 International Conference on Physics
and Its Applications, ICPAP 2011Influence of Calcination Temperatures on Physics Properties of Magnetic and electrical Material Produced by Sol Gel Auto Combustion.
2011, ITB Bandung
4 Seminar Nasional Material 2012 Pergeseran Pola Difraksi Sinar – X Pada Material Feromagnetik dan Feroelektrik.
2012, ITB Bandung
5 International Conference on Advances in Manufacturing and Materials Engineering, ICAMME 2012
Shifting of X-Ray Diffraction Pattern Peak on BaFe12O19
Nanocrystalline Produced by Sol-Gel Auto Combustion Method
3-5 Juli 2012, Kuala Lumpur, Malaysia
6 Seminar Hasil-hasil Penelitian, Pengabdian dan Pemberdayaan Masyarakat Institut Teknologi Indonesia
Metode Sol-Gel pada Sintesa Material Nanokomposit
27 November 2013, Serpong
7 Seminar Nasional Material 2013 Pengaruh Perlakuan Sinter Ganda Terhadap Sifat Magnetik Nanokomposit Berdasarkan Perbedaan Fraksi Volume dan Waktu Sinter
2013, ITB Bandung
8 The 13th International Conference QiR (Quality in Research), 2013
Nanosize Effects on Magnetic Properties and Peak Shifting of X-Ray Diffraction Pattern of BaFe12O19
Produced by Sol-Gel
25 – 28 Juni 2013, Jogjakarta, Indonesia
27
Method.9 The 13th International Conference
QiR (Quality in Research), 2013Magnetic Behaviors of Nanocomposite Based on Differences in Volume Fraction Prepared by Sol-Gel.
25 – 28 Juni 2013, Jogjakarta, Indonesia
10 International Conference on Mechanical Engineering 2013 (ICOME 2013
Simple Recipe to Synthesize BaTiO3-BaFe12O19
Nanocomposite Bulk System With High Magnetization
12 – 14 September 2013, Lombok, Indonesia
11 The 2013 International Conference on Advanced Materials Science and Technology, 2013
Magnetoelectric Coupling Phenomena Based on The Changes of Magnetic Properties in Multiferroic NanocompositeBaTiO3-BaFe12O19
System
17 – 18 September 2013, Jogjakarta, Indonesia.
12 Seminar Nasional Fisika 2014 Sintesa dan Karakteristik Elektrik Barium Titanate Nanopartikel Fasa Tunggal dengan Metode Sol-Gel.
26 April 2014, Jogjakarta, Indonesia
13 Seminar Nasional Sains an Pendidikan Sains IX “Kemajuan Iptek dan Implementasi Kurikulum 2013”
Karakteristik Elektrik Nanopartikel BaTiO3
untuk Aplikasi Material Multiferroic
21 Juni 2014, Salatiga
14 Seminar Nasional Inovasi Teknologi dan Rekayasa Industri (SINTERIN) 2104, Universitas Andalas Padang, Sumatera Barat
Metode Sol-Gel pada Sintesa Material Feroelektrik Barium Titanate
26 Agustus 2014, Universitas Andalas, Sumatera Barat (Pangeran Beach Hotel)
28
Nanopartikel Fasa Tunggal
15 International Conference on Advance Materials Science and Technology (ICAMST 2014)
Characterization of Nanocomposite Multiferroic Material Based on Ferroelectric and Ferromagnetic Materials
16 September 2014, Universitas Sebelas Maret, Solo (Lorin Hotel)
S. Pengalaman Sebagai Peserta Kegiatan Ilmiah / Seminar / Workshop / PelatihanNo Nama Kegiatan Penyelenggara Waktu dan Tempat1 Peserta Sosialisasi Standardisasi Bagi
Dosen dan MahasiswaBadan Standardisasi Nasional (BSN)
ITI-Serpong, 23 April 2014
T. Pengalaman Penulisan Buku Dalam 5 Tahun Terakhir
No Judul Buku Tahun Jumlah Halaman Penerbit12
U. Pengalaman Perolehan HKI Dalam 5 – 10 Tahun TerakhirNo Judul / Tema HKI Tahun Jenis Nomor P/ID12
V. Pengalaman Merumuskan Kebijakan Publik/Rekayasa Sosial Lainnya Dalam 5 Tahun Terakhir
No Judul/Tema/Jenis RekayasaSosial Lainnya yang Telah Diterapkan
Tahun Tempat Penerapan
Respons Masyarakat
1 Pemetaan Investasi Untuk Industri Kimia dan Turunannya
2009-2010
Propinsi Jawa Timur
Baik
2 Pemetaan Investasi Untuk Industri Manufaktur
2009-2010
Propinsi Jawa Timur, Sumatera Utara
Baik
29
dan Sulawesi Utara
3 Pemetaan Pengembangan Industri Bahan Kimia Khusus Berbasis Hasil Samping dan atau Limbah Industri CPO dan turunannya
2010-2011
Propinsi Jawa Timur
Baik
4 Penyusunan Kurikulum Pendidikan Hard Skill dan Soft Skill Bidang Otomotif Roda Dua Untuk Para Santri Pondok Pesantren.
2011-2012
Pondok Pesantren Tremas, Pacitan Jawa Timur
Baik
5 Kajian Desk Research untuk Komoditi Timah Sebagai Subyek Sistem Resi Gudang (SRG)
2014 Provinsi Kepulauan Bangka Belitung
Baik
W. Penghargaan Yang Pernah Diraih Dalam 10 Tahun Terakhir (Dari Pemerintah, Asosiasi atau Institusi Lainnya)
No Jenis Penghargaan Institusi Pemberi Penghargaan
Tahun
1 Sertifikat Pendidik nomor 08161209494
Departemen Pendidikan Nasional Republik Indonesia
2008
Semua data yang saya isikan dan tercantum dalam biodata ini adalah benar dan dapat dipertanggungjawabkan secara hukum. Apabila di kemudian hari ternyata dijumpai ketidaksesuaian dengan kenyataan, saya sanggup menerima resikonya.
Tangerang Selatan, 25 September 2014
(Dr.Ir. Dwita Suastiyanti,M.Si)
30
Lampiran 2. Justifikasi Anggaran Kegiatan1. Peralatan Menunjang
Uraian Justifikasi Pemakaian
Kuantitas(sampel)
Harga Satuan (Rp)
Total(Rp)
Analisa XRD Jasa uji 9 150.000 1.350.000
Analisa SEM Jasa uji 9 150.000 1.350.000Analisa PSA Jasa uji 9 paket 425.000
SUBTOTAL (Rp) 3.125.000
2. Bahan Habis Pakai
Material Justifikasi Pemakaian
Kuantitas Harga Satuan (Rp)
Total(Rp)
Al(NO3)3.9H2O Bahan dasar
3x250 gram 925.000 2.775.000
NH4OH Bahan dasar
1 botol (2,5 liter)
625.000 625.000
Citric Acid (C6H8O7 / asam sitrat)
Fuel 1x 500 gram 725.000 725.000
Aqua bidestilata Pelarut 10 botol 25.000 250.000
SUBTOTAL (Rp) 4.375.0003. Perjalanan
Tujuan Justifikasi Perjalanan
Kuantitas Harga Satuan (Rp)
Total(Rp)
Jakarta- Bandung
Mengikuti seminar nasional
1 750.000 750.000
Jakarta-Jogjakarta
Mengikuti seminar
nasional dan studi banding
ke UGM Jogjakarta
2 1.000.000 2.000.000
Dalam kota (Jakarta-Serpong)
Perjalanan pembelian
bahan-bahan kimia
1 375.000 375.000
31
SUBTOTAL (Rp) 3.125.000
4. Lain-lain
Uraian Justifikasi Pemakaian
Kuantitas Harga Satuan (Rp)
Total(Rp)
Registrasi seminar nasional
Pendaftaran Pemakalah
pada seminar nasional
2x 500.000 1.000.000
Fotokopi Penggandaan laporan dan
referensi
250 lembar 200 50.000
Pembelian tinta printer
Untuk cetak (print out)
laporan
2 buah 200.000 400.000
Komunikasi (Internet, tlp, fax dll)
Browsing referensi,
komunikasi dengan dosen pembimbing
paket 350.000 350.000
Pembelian kertas A4 (80 gram/m2)
Pembuatan laporan
2 rim 37.500 75.000
SUBTOTAL (Rp) 1.875.000
Keterangan Biaya Keseluruhan :
Peralatan penunjang : Rp 3.125.000,- Biaya habis pakai : Rp 4.375.000,- Biaya transportasi : Rp 3,125.000,- Biaya lain-lain : Rp 1.875.000 +
Rp 12.500.000,-
32
Lampiran 3.Susunan Organisasi Tim Peneliti dan Pembagian Tugas
No Nama / NIM Program Studi
Bidang Ilmu
Alokasi Waktu
(Jam/Minggu)
Uraian Tugas
1 Nikko Eddy Sugianto/114120002
Teknik Kimia Kimia
2 Dwi Ratna Mustafida/114120003
Teknik Kimia Kimia
3 Didit Eko Prasetyo /114130034
Teknik Kimia Kimia
4 Eka Fitriyani / 114130035
Teknik Kimia Kimia